ISOTHANE FR - Halogen-Free / Flame Retardant Grade

Tên Hạng mụcISOTHANE FR - Halogen-Free / Flame Retardant Grade
Đặc tính sản phẩm ISOTHANE® FR series products are thermoplastic polyurethane containing halogen-free fire retardant. They not only offer excellent flame retardancy, but also possess good mechanical properties, hydrolytic stability, low temperature flexibility and abrasion resistance. ISOTHANE® FR series can be processed by extrusion and injection molding.
Trường hợp sử dụng Building/Construction, Mining, Wire andCables
Item NameHalogen-Free / Flame Retardant Grade
Description ISOTHANE 8800 series products have good initial adhesive strength, fast crystallization, good solubility, good washing durability and freezing resistance etc.. Viscosity ranges from 150~2800cps (15% MEK Solution), and viscosity could be customized for different viscosity. They exhibit good adhesive with TPU, PVC, polyester fabric, leather and other materials.
Supply and Storage ISOTHANE TPU resins are supplied in pellet form packed in 25kg moisture proof bags. All TPU resins have been dried before packing. ISOTHANE TPU resins should be stored in cool and dry environment in their original containers until be used. Storage temperature should not exceed 30°C. If only a portion of TPU resins was used from a bag, the remainder of TPU resins should be tightly closed.
Drying TPU resins are hygroscopic and pre-drying of TPU resins is always a necessary step before processing. Depend on the climate, the granule exposed to the atmosphere will absorb moisture very quickly. The moisture might bring about partial degradation of polymers and the formation of bubbles or streaks in the molded and extruded parts. In order to ensure the efficient and successful processing into quality parts, the moisture content in TPU resins is recommended less than 0.02%.

A desiccant-bed-type hopper dryer is recommended for drying ISOTHANE TPU. The dew point of the inlet air should be in the range of -30 to -40°C. About the recommended drying conditions, please view ISOTHANE individual data sheets.
Processing - Extrusion Barrel and Motor
  • High torque drive capacity at low speed
  • Vented or standard barrels acceptable
Screw
  • Compression ratios between 2:1 and 3:1
  • Minimum L/D of 30/1
Feed Throat
  • Vertical and tangential
  • Water cooling is recommended
Screen Pack
  • Streamlined breaker plates with screen packing is recommended
  • Typical 40/80/80/40 mesh screens
Die
  • Streamline with good temperature control
  • Land Length is generally 10 to 15 times the part thickness
  • Coat-hanger manifold-type dies are recommended for extruding film and sheet
  • Crosshead dies are recommended for wire, cable and hose jacketing
  • Side-fed rotating dies are recommended for blown film
About the recommended extrusion temperatures, please view ISOTHANE individual data sheets.
Processing - Injection Molding Barrel and Motor
  • High torque drive capacity at low speed
  • Vented or standard barrels acceptable
Screw
  • Compression ratios between 2:1 and 3:1
  • Metering screw with gradual transition zone
Injection Pressure
  • Typical 6,000 to 15,000 psi
  • Hold pressure 60 – 70% of forward time
Injection speed
  • Slow to moderate
  • Depends on gating, wall section and flow length
About the recommended injection molding temperatures, please view ISOTHANE individual data sheets.
Coloring Generally, ISOTHANE TPU resins are supplied in their natural color. They can be colored by blending with pigment or pigment master batch. Using master batch based on TPU is recommended. Other master batch based on polyethylene or polystyrene is suitable to a limited extent. All colorants employed in TPU resins must be pre-dried before processing.

The normal addition of pigment or pigment master batch is 0.2%-0.5% or 1-3%.
Additives Various additives can be used to enhanced the properties of ISOTHANE TPU resins, e.g. anti-blocking agents, antioxidant, UV stabilizers or release agents. Most additives supplied as master batches are available. But not all additives are compatible with ISOTHANE TPU resins. It is recommended to inquire of your suppliers or our technical service before compounding.
Recycling For ISOTHANE TPU resins, up to 20% of regrind may be recycled with virgin material depending on finished parts requirements. The regrind material has to be kept free of contamination, diced and dried before re-using. The material which has been contaminated, discolored or degraded is not suitable for recycling. TPU resins may decrease desired properties, e.g. hardness and mechanical properties, due to improperly mixing with regrind.
Regulatory or testing organizations (e.g., UL) may have specific requirements limiting the allowance amount of regrind. Certain quality requirements laid down in specifications may exclude the use of regrind material.
Healthy and Safety Information Before working with these products, it is essential that all operators are aware of the healthy and safety precautions. ISOTHANE TPU resins can be processed or machined over a wide range of temperature. There can be some smoke formation during processing. The smoke that contains some decomposition substances of TPU or additives may cause irritation to human body. Generally, the temperature does not exceed 240°C that can reduce decomposition formation. An effective extraction system, especially in the melt outlet zone, is necessary. The detail information concerning healthy and safety can be available in safety data sheets (SDS) or contact our technical service.
Disposal ISOTHANE TPU resins present no hazard to the environment or water. They can be dumped on municipal landfill or in a waste incineration plant. The official regulations on waste disposal should be observed.
Hạng mụcUnitsASTMPolyester FR-TPU
1085A-FR1085A-FRT1090A-FR
Specific Gravity   D-792 1.18 1.20 1.20
Hardness Shore A    D-2240 84A 85A 90A
Tensile Strength MPa
psi
D-412 32
4,620
36
5,260
35
5,120
@ 50% Elongation MPa
psi
D-412 4
570
4
570
8
1,140
@ 100% Elongation MPa
psi
5
780
5
710
9
1,280
@ 300% Elongation MPa
psi
11
1,560
10
1,420
14
2,000
Elongation @ Break % D-412 610 600 600
Tear Strength N/mm
lb/in
D-624
DIE C
110
620
110
620
150
840
Flammability (2mm) - UL-94 V-0 V-0 V-0
Appearance - - White Transparent White
Hạng mụcUnitsASTMPolyether FR-TPU
3080A-FR3085A-FR3085A-FRT3085A-FRC3090A-FR3095A-FR
Specific Gravity   D-792 1.15 1.15 1.18 1.20 1.15 1.18
Hardness Shore A D-2240 80A 85A 84A 85A 91A 94A
Tensile Strength MPa
psi
D-412 20
2,920
29
4,270
33
4,840
15
2,130
30
4,400
25
3,560
@ 50% Elongation MPa
psi
D-412 4
640
6
850
4
640
6
920
10
1,420
10
1,500
@ 100% Elongation MPa
psi
6
850
8
1,140
6
850
7
1,070
12
1,710
12
1,710
@ 300% Elongation MPa
psi
10
1,420
13
1,850
11
1,560
9
1,280
19
2,770
19
2,700
Elongation @ Break % D-412 610 570 700 710 480 400
Tear Strength N/mm
lb/in
D-624
DIE C
93
530
130
730
120
670
110
620
133
750
130
730
Flammability (2mm) - UL-94 V-0 V-0 V-0 V-0 V-0 V-0
Appearance - - White White Transparent White White White

These property values under specific test conditions as defined in the table above are for reference only.