Dòng ISOTHANE 7000 - Aliphatic Grade

Tên Hạng mụcAliphatic Grade
Đặc tính sản phẩm ISOTHANE® 7000 series products are aliphatic grade thermoplastic polyurethane having high elasticity and transparency. They exhibit excellent mechanical properties, abrasion resistance, hydrolysis resistance and no yellowing on exposure to UV light. ISOTHANE® 7000 series can be processed by extrusion and injection molding.
Trường hợp sử dụng Automotive Protective Films and Smart Wearable Devices
Item NameAliphatic Grade
Description ISOTHANE 7000 series products are aliphatic grade thermoplastic polyurethane having high elasticity and transparency. They exhibit excellent mechanical properties, abrasion resistance, hydrolysis resistance and no yellowing on exposure to UV light. ISOTHANE 7000 series can be processed by extrusion and injection molding.
Supply and Storage ISOTHANE TPU resins are supplied in pellet form packed in 25kg moisture proof bags. All TPU resins have been dried before packing. ISOTHANE TPU resins should be stored in cool and dry environment in their original containers until be used. Storage temperature should not exceed 30°C. If only a portion of TPU resins was used from a bag, the remainder of TPU resins should be tightly closed.
Drying TPU resins are hygroscopic and pre-drying of TPU resins is always a necessary step before processing. Depend on the climate, the granule exposed to the atmosphere will absorb moisture very quickly. The moisture might bring about partial degradation of polymers and the formation of bubbles or streaks in the molded and extruded parts. In order to ensure the efficient and successful processing into quality parts, the moisture content in TPU resins is recommended less than 0.02%.

A desiccant-bed-type hopper dryer is recommended for drying ISOTHANE TPU. The dew point of the inlet air should be in the range of -30 to -40°C. About the recommended drying conditions, please view ISOTHANE individual data sheets.
Processing - Extrusion Barrel and Motor
  • High torque drive capacity at low speed
  • Vented or standard barrels acceptable
Screw
  • Compression ratios between 2:1 and 3:1
  • Minimum L/D of 30/1
Feed Throat
  • Vertical and tangential
  • Water cooling is recommended
Screen Pack
  • Streamlined breaker plates with screen packing is recommended
  • Typical 40/80/80/40 mesh screens
Die
  • Streamline with good temperature control
  • Land Length is generally 10 to 15 times the part thickness
  • Coat-hanger manifold-type dies are recommended for extruding film and sheet
  • Crosshead dies are recommended for wire, cable and hose jacketing
  • Side-fed rotating dies are recommended for blown film
About the recommended extrusion temperatures, please view ISOTHANE individual data sheets.
Processing - Injection Molding Barrel and Motor
  • High torque drive capacity at low speed
  • Vented or standard barrels acceptable
Screw
  • Compression ratios between 2:1 and 3:1
  • Metering screw with gradual transition zone
Injection Pressure
  • Typical 6,000 to 15,000 psi
  • Hold pressure 60 – 70% of forward time
Injection speed
  • Slow to moderate
  • Depends on gating, wall section and flow length
About the recommended injection molding temperatures, please view ISOTHANE individual data sheets.
Coloring Generally, ISOTHANE TPU resins are supplied in their natural color. They can be colored by blending with pigment or pigment master batch. Using master batch based on TPU is recommended. Other master batch based on polyethylene or polystyrene is suitable to a limited extent. All colorants employed in TPU resins must be pre-dried before processing.

The normal addition of pigment or pigment master batch is 0.2%-0.5% or 1-3%.
Additives Various additives can be used to enhanced the properties of ISOTHANE TPU resins, e.g. anti-blocking agents, antioxidant, UV stabilizers or release agents. Most additives supplied as master batches are available. But not all additives are compatible with ISOTHANE TPU resins. It is recommended to inquire of your suppliers or our technical service before compounding.
Recycling For ISOTHANE TPU resins, up to 20% of regrind may be recycled with virgin material depending on finished parts requirements. The regrind material has to be kept free of contamination, diced and dried before re-using. The material which has been contaminated, discolored or degraded is not suitable for recycling. TPU resins may decrease desired properties, e.g. hardness and mechanical properties, due to improperly mixing with regrind.
Regulatory or testing organizations (e.g., UL) may have specific requirements limiting the allowance amount of regrind. Certain quality requirements laid down in specifications may exclude the use of regrind material.
Healthy and Safety Information Before working with these products, it is essential that all operators are aware of the healthy and safety precautions. ISOTHANE TPU resins can be processed or machined over a wide range of temperature. There can be some smoke formation during processing. The smoke that contains some decomposition substances of TPU or additives may cause irritation to human body. Generally, the temperature does not exceed 240°C that can reduce decomposition formation. An effective extraction system, especially in the melt outlet zone, is necessary. The detail information concerning healthy and safety can be available in safety data sheets (SDS) or contact our technical service.
Disposal ISOTHANE TPU resins present no hazard to the environment or water. They can be dumped on municipal landfill or in a waste incineration plant. The official regulations on waste disposal should be observed.
Hạng mụcUnitsASTMPolyester TPUPolycaprolactone TPU
7185A7190A7195A7285A7290A-E
Độ cứng   D-792 1.16 1.16 1.18 1.12 1.11
Độ mạnh kháng kéo Shore A  D-2240 85A 90A 95A 85A 90A
Tỷ lệ kéo dài MPa
psi
D-412 27
3930
33
4790
44
6380
23
3780
23
3340
@ 50% số lượng màng kháng kéo MPa
psi
7
1020
7
1020
14
2030
5
725
6
870
@ 100% số lượng màng kháng kéo MPa
psi
9
1310
11
1600
15
2180
7
1020
7
1020
@ 300% số lượng màng kháng kéo MPa
psi
19
2780
21
3050
24
3490
13
1890
17
2470
Tỷ lệ kéo dài bị đứt % 600 550 500 650 450
Độ cứng xé rách N/mm
lb/in
D-624
DIE C
165
925
180
1010
220
1240
135
760
120
675
Hạng mụcUnitsASTMPolyether TPU
7380A-E7385A7385A-E7390A-E
Độ cứng   D-792 1.08 1.04 1.08 1.08
Độ mạnh kháng kéo Shore A  D-2240 80A 85A 85A 90A
Tỷ lệ kéo dài MPa
psi
D-412 42
6090
31
4500
43
6090
45
6530
@ 50% số lượng màng kháng kéo MPa
psi
5
725
5
725
6
870
8
1160
@ 100% số lượng màng kháng kéo MPa
psi
8
1160
6
870
9
1310
10
1450
@ 300% số lượng màng kháng kéo MPa
psi
31
4500
10
1450
35
5080
39
5660
Tỷ lệ kéo dài bị đứt % 400 700 400 430
Độ cứng xé rách N/mm
lb/in
D-624
DIE C
110
620
140
785
115
645
120
675

These property values under specific test conditions as defined in the table above are for reference only.